Latex Examination Gloves
Superior Hand Protection for Effective Contamination Control
Dynawell Latex Examination Gloves (Powder-Free) offer superior yet affordable protection for your hands. Being powder-free, each of our gloves has undergone a proprietary polymer coat and surface treatment to ensure easy donning by users. Dynawell Latex Examination Gloves (Powder-Free) meet global standards for medical gloves. They also fulfil all regulatory requirements for biocompatibility testing.
Features:
- Specially formulated for superior barrier protection with low allergenic protein content
- Polymer coat and surface treated for maximum ease of donning
- Ambidextrous shape for maximum comfort during extended use
- Biocompatibility tested to ISO 10993 standard
| DYNAWELL DISPOSABLE LATEX EXAMINATION GLOVES (POWDER-FREE) (ITEM CODE: XXXX) PRODUCT STANDARD SPECIFICATIONS, PERFORMANCE & CONFORMANCE | |
| Type | Disposable, Powder-Free Latex Examination Gloves |
| Material | Natural Rubber Latex (NR) |
| Colour | Natural Chlorinated |
| Design and Features | Ambidextrous, Beaded Cuff, Palm Textured |
| Donning Aid | Chlorinated/Polymer Coated |
| Powder Content | Max 2.0 milligrams/glove |
| Protein Content | Max 50 micrograms/dm2 |
| Available Sizes | XS, S, M, L, XL, XXL |
| Storage Conditions | Room conditions, away from direct sunlight |
| Shelf Life | 3 years from manufacture date, with the above storage conditions |
| Packing Style | 100 pieces/dispenser, 10 dispensers/carton |
| Performance Standards | ASTM D-3578 EN 455-Parts 1, 2 and 3 |
| PHYSICAL DIMENSIONS – 4 MILS, 240 MILLIMETRES/9 INCHES | ||||||
| Size | XS | S | M | L | XL | XXL |
| Average width (mm) | 78±2 | 85±5 | 95±5 | 106±5 | 113±5 | 120±5 |
| Average weight (gm) | 5.0±1.0 | 5.5±1.0 | 6.0±1.0 | 6.5±1.0 | 7.0±1.0 | 7.5±1.0 |
| Length (mm) | Min 240 | |||||
| Thickness | Cuff Palm Finger | 0.08±0.02 0.110±0.02 0.120±0.03 | ||||
| PHYSICAL PROPERTIES – ASTM | ||||||
Parameters | Before Aging | After Aging | ||||
| Tensile Strength (MPa) | Elongation at break (%) | Modulus at 500% (MPa) | Tensile Strength (MPa) | Elongation at break (%) | Modulus at 500% (MPa) | |
| Dynacare’s Results | 18-22 | 650-750 | 4.0-5.5 | 14-18 | 500-700 | 4.0-5.5 |
| ASTM Requirements | Min 18 | Min 650% | Max 5.5 | Min 14 | Min 500% | N/A |
| PHYSICAL PROPERTIES – EN | ||||
Parameters | Before Aging | After Aging | ||
| Tensile Strength (N) | Elongation at Break (%) | Tensile Strength (N) | Elongation at Break (%) | |
| Dynacare’s Results | 9.0-11.0 | N/A | 6.0-9.0 | N/A |
| EN Requirements (median) | Min 6N | N/A | Min 6N | N/A |
| CHEMICAL ANALYSIS | ||
| Protein Content | Powder Content | |
| Dynacare’s Results | Below 50 micrograms/dm2 | Below 2.0 milligrams/glove |
| ASTM Requirements | Max 50 micrograms/dm2 | Max 2.0 milligrams/glove |
| PERFORMANCE | |||
| Inspection | Related Defects | Inspection Level | AQL |
| Watertight Test | Holes | G-1 | 1.5 |
Visual Inspection | Major Defects | 2.5 | |
| Minor Defects | 4 | ||
| Physical Properties | Tensile Strength and Elongation | S-2 | 4 |
| Physical Dimensions | Measurement | S-2 | 4 |